1. The water flux of pan / pu hollow fiber membranes increased with the increase of draw ratio and concentration of pan
   Pan pu中空纖維膜的的水通量隨著拉伸倍數(shù)的增大而增大，隨著pan含量的增大而增大。
2. The results indicate that : ( 1 ) as the drawing ratio increase , the mechanical properties , crystallinity and orientation of uhmwpe fiber all increase greatly , while the average crystal size decreases
   結果表明:隨拉伸的進行， uhm筋胭e纖維的力學性能、結晶度、取向度均大大提高，而晶粒尺寸逐漸變小。
3. While polyester fiber is subject to different draw ratio and heating temperature during high speed spin - fling , its original molecular orientation and crystallinity of polyester fiber are changed
   摘要聚酯在高速紡絲過程中，施以不同的拉伸倍數(shù)與溫度，會造成纖維結晶度與取向度的變化，從而影響纖維的物理性能。
4. Polyester petg sheet has outstanding thermoforming properties , combining low energy consumption , short production cycles , extreme draw ratios and good mould reproduction without the need for pre - drying
   公司愿以先進的技術，可靠的質(zhì)量保證和真誠的合作態(tài)度為客戶提供最優(yōu)最滿意的服務，我們真誠地期待您的惠顧。
5. This paper investigated the physical properties of polyester filament yarn such as tenacity , elongation and boiled water shrinkage by means of analyzing the poy which had been treated by different draw ratio and heating temperature
   通過對不同拉伸倍數(shù)及不同溫度處理的poy的分析，探討長絲紗的強度、伸長度及沸水收縮率等物理機械性質(zhì)。
6. It's difficult to find drawing ratio in a sentence. 用drawing ratio造句挺難的
7. When polyester fiber is subject to different draw ratio and heating temperature during high speed spinning , it will result in changes of the original molecular orientation and crystallinity of the fiber , thus affecting its physical properties
   摘要在高速紡絲過程中對聚酯施以不同的拉伸倍數(shù)與溫度，會造成纖維結晶度與取向度的變化，從而影響纖維的物理性能。
8. The influence of the melt transfer temperature , spinning temperature , temperature and speed of quench air , the 1st hot rolls temperature , the 3th hot rolls temperature , drawn ratio on dying property of melt direct spun fdy were discussed
   摘要主要就熔體直接紡fdy生產(chǎn)過程中熔體輸送溫度、紡絲溫度、側吹風溫度、風速、第一對熱輥溫度、第三對熱輥溫度、拉伸倍數(shù)等因素對染色性能的影響進行探討。
9. The a phase can change to b phase by stretching . in the range of low temperature the higher content of b crystalline was achieved during the higher drawing ratio and the higher drawing temperature
   拉伸有利于pvdf纖維的相結晶向相結晶轉(zhuǎn)變，且拉伸倍數(shù)越高相含量越高；較低溫度區(qū)域內(nèi)( 100 ) ，溫度提高有利于相結晶向相轉(zhuǎn)變，較高溫度區(qū)域內(nèi)( 100 ) ，溫度提高對相向相轉(zhuǎn)變作用不大。